Abstract
Tritium release behavior for thermal neutron-irradiated Li0.17Pb0.83 eutectic alloy was studied. Main tritium release peak was observed in the temperature just a little higher than melting point in a thermal desorption spectrometry (TDS) experiment. Most of tritium release from Li0.17Pb0.83 eutectic alloy was found to be governed by diffusion process from the results of isothermal annealing experiments. Tritium diffusivity in a liquid state of Li0.17Pb0.83 eutectic alloy was evaluated to be D = 4.7 × 10-8 exp(-0.13 eV/kT) m2 s-1. Tritium diffusivity was increased by the phase transition of Li0.17Pb0.83 eutectic alloy from a solid state to a liquid state, resulting in the sharp tritium release peak that appeared in TDS spectrum. In addition, about 4% of tritium was trapped in Li0.17Pb0.83 eutectic alloy as Li-T bond.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.