Abstract
Abstract The examined material comprised two grades of corrosion-resistant cast steel, namely GX2CrNiMoN25-6-3 and GX2CrNiMoCuN25-6-3- 3, used for example in elements of systems of wet flue gas desulphurisation in power industry. The operating conditions in media heated up to 70°C and containing Cl' and SO4 ions and solid particles produce high erosive and corrosive wear.The work proposes an application of the σ phase as a component of precipitation strengthening mechanism in order to increase the functional properties of the material. The paper presents the results of examination of the kinetics of σ phase precipitation at a temperature of 800°C and at times ranging from 30 to 180 minutes. Changes in the morphology of precipitates of the σ phase were determined using the value of shape factor R. Resistance to erosion-corrosion wear of duplex cast steel was correlated with the kinetics of sigma phase precipitating.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.