Abstract
The influence of thermal action at 1150 °C on the kinetics of phase transformations in a layered coating FeAl (Cr,Si) / Fe3Al (Cr,Si) / Fe (Al,Cr,Si), obtained using a technology involving aluminizing of an Cr15Al5 alloy by hot dipping in silumin melt AK12M2 and heat treatment. It was shown that after 100 hours of exposure, the visually distinguishable boundary between the coating and the alloy disappears. The aluminum content in the Cr15Al5 alloy increased to 17 at. %, silicon up to 3 at. %, and chromium is reduced to 14 at. %. The microhardness of the alloy increases from 1.6 to 2.4 GPa and survivability at a test temperature of 1150 °C increases from 120 to at least 920 hours.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.