Abstract

On different As-rich GaAs(001) templates, well characterized by reflectance difference spectroscopy, nucleation and growth of NiAs-type MnAs is investigated in real time by reflection high-energy electron diffraction. Using very high As4/Mn flux ratios and low growth rates, one of the two occurring azimuthal alignments of the (1̄100) orientation can be nearly suppressed even in the nucleation stage, and it vanishes completely with further growth. Annealing is found to be very effective in surface smoothing. In dependence on the As/Mn ratio the MnAs(1̄100) surface develops different reconstructions. This finding is important for further investigations in the growth of double heterostructures. High-resolution transmission electron microscopy of as-grown MnAs/GaAs samples reveals an abrupt interface. The lattice mismatch accommodation is anisotropic with regularly arranged misfit dislocations along the [1̄10] direction and less localized coherency strain in the [110] direction, consistent with a near-coincidence-site lattice model.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.