Abstract
Thermal stability of Si(0.8)Ge(0.2)/Si(001) virtual substrates (VS) is studied as a function of annealing temperature and time by X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM). Two regimes describing different Ge behavior are observed when the Si(0.8)Ge(0.2) VS is annealed. Heating the substrate from room temperature to 500 degrees C results in some degree of Ge segregation. The surface morphology however remains relatively smooth and there is no formation of 3D islands on the surface. Above 500 degrees C, Ge is preferentially lost from the surface and microscopic pits with edges aligned along 110 azimuth are formed. As temperature increases, Ge% decreases and the size of pits also increases. The decrease in Ge% and the formation of holes at the surface are attributed to Ge desorption from the surface. A kinetic model involving diffusion and desorption processes is proposed to describe the Ge behavior and pits formation in this regime.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.