Abstract

The extremely high adsorption efficiency of malachite green (MG) was examined through a series of batch experiments by using Fe3+-doped Mg/Al layered double hydroxides (LDHs). The incorporation of iron into Mg/Al LDH with varying Al + Fe molar ratio of 4 + 1, 3 + 2, 2 + 3, and 1 + 4 increased the adsorption capacity with respect to time. The spectral analysis and N2 sorption studies showed that there was retention of surface morphology in all of the iron-modified LDH samples. The experimental evidences showed that the adsorbent Mg/(Al + Fe) with a molar ratio of 10:2 + 3 had a significant removal, i.e., 99.94% for MG with the initial concentration of 1000 mg L–1 at pH ∼ 9 and at room temperature in 5 min. With further increase in iron loading (at ratio 10:1 + 4), there was a decrease in the removal of MG due to the agglomeration of Fe2O3 on the surface. The adsorption process was best fitted to the Freundlich isotherm followed by the pseudo-second-order model. The standard thermodynamic parameters (ΔH°, ΔS°, and ΔG°) were obtained over the temperature range of 20–50 °C. It was observed that the adsorption of MG onto Mg/(Al + Fe) LDH was spontaneous, exothermic, and enthalpy driven in the physisorption mode. A worthy desorption efficiency was achieved by using ethanol and water, which was more than 90% in the three cycles. Maintaining almost the same removal efficiency of MG even after three cycles indicated Mg/(Al + Fe) LDH as a promising material for wastewater treatment. This work was anticipated to open up new possibilities in dealing with anionic dye pollutants.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call