Kinetic study of the carbothermic synthesis of uranium monocarbide microspheres

Abstract

Abstract Uranium monocarbide microspheres were synthesized by carbothermic reduction of porous uranium oxide microspheres with uniformly dispersed carbon black. Kinetics of the reduction was studied under vacuum and flowing inert gas from 1250 to 1550° C. The carbon monoxide gas concentration in the effluent stream during reduction was used to determine the rate of carbide formation. Under vacuum, reduction was found to be controlled by reaction at the reactant-product interface whereas under flowing gas conditions, the diffusion of carbon monoxide gas through the carbide layer was the rate controlling process. The activation energy was 335.1 ± 8.6 and 363.7 ± 7.6 kJ/mol for reduction under vacuum and flowing gas, respectively.