Kinetic investigations of acrylic–polyurethane composite latex

Abstract

AbstractThe effect of various reaction parameters on the rate of polymerization, Rp, and on the particle size and morphology of aqueous acrylic–polyurethane hybrid dispersions, prepared by semibatch emulsion polymerization, was investigated. The particles of polyurethane dispersion were used as seeds during the polymerization of acrylic component: methyl methacrylate (MMA), butyl acrylate (BA), and a mixture of MMA and BA with the ratio of 1:1. These emulsions were found to form structured polymer particles in aqueous media using scanning electron microscopy. The kinetics of the emulsion polymerization was studied on the basis of Wessling's model. The influence of emulsifier and initiator concentrations, including the monomer feed rates, Rm, on the rates of polymerization and on the properties of the resulting dispersions were studied. The number of particles and the particle size were also measured during the polymerization process. The final values were found to be independent of the concentration of the emulsifier, initiator and the monomer feed rate in monomer starved conditions. In the steady‐state conditions, during the seeded semibatch hybrid emulsion polymerization, the rate of polymerization and the monomer feed rate followed the Wessling relationship 1/Rp = 1/K + 1/Rm. The dispersions MMA/PU, BA/PU, and MMA/BA/PU have K values of 0.0441, 0.0419 and 0.0436 mol/min, respectively. The seeded BA/PU hybrid polymerization proceeded according to Smith‐Ewart Case I kinetics, while the MMA/PU hybrid emulsions demonstrate Case II of the Smith‐Ewart kinetic model. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 2639–2649, 2002