Abstract
Abstract The Al 2 O 3 /Cu composite was prepared by mechanical activation and internal oxidation process. Kinetic factors, which influenced the internal oxidation process, were also discussed in the present paper. The results showed that the duration of the internal oxidation was highly shortened after the powders were treated by mechanical activation. The typical internal oxidation duration was only 1 h. It is unnecessary for further prolonging internal oxidation time. Besides, in order to get a complete internal oxidation heating rate and green density of the compact are another two control factors. Their parameters should be controlled from Al contents in the powders. In this research, the optimum internal oxidation duration, heating rate and green density are 1 h, 20 °C/min and 80%, respectively, for Cu–0.8 wt% Al/Cu 2 O powders. After the internal oxidation, uniform spherical α-Al 2 O 3 particles with an average size 0.5–0.8 μm in diameter were observed in the Cu matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Composites Part A: Applied Science and Manufacturing
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.