Abstract
The crystallization kinetics of [(Fe0.5Co0.5)0.75B0.2Si0.05]96Nb4 and {[(Fe0.5Co0.5)0.75B0.2Si0.05]0.96Nb0.04}99.5Cu0.5 bulk metallic glasses were evaluated using differential scanning calorimetry under non-isothermal condition. The fully glassy rods with diameters up to 2 mm were obtained by copper mold injection casting. Both glasses show good thermal stability, but the addition of only 0.5% Cu completely changes the crystallization behavior. The average activation energy required for crystallization decreases from 645 kJ/mol to 425 kJ/mol after Cu addition. Upon heating, the Cu-free alloy forms only the metastable Fe23B6 phase. In contrast, two well-separated exothermic events are observed for the Cu-added bulk glassy samples. First, the (Fe,Co) phase nucleates and then (Fe,Co)2B and/or (Fe,Co)3B crystallize from the remaining glassy matrix. The Cu-added alloy exhibits a lower coercivity and a higher magnetic saturation than the base alloy, both in as-cast as well as in annealed condition. Besides, the Cu-added glassy sample with 2 mm diameter exhibits a maximum compressive fracture strength of 3913 MPa together with a plastic strain of 0.6%, which is highest plastic strain ever reported for 2 mm diameter ferromagnetic bulk metallic glass sample. Although Cu addition improves the magnetic and mechanical properties of the glass, it affects the glass-forming ability of the base alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.