Kinetic analysis of the crystallization of poly( p-phenylene sulphide)

Abstract

Growth rates of spherulites were measured in poly( p-phenylene sulphide) crystallized from the melt and the quenched glass over the temperature range 100°C–280°C, possibly the most extensive overall range yet reported for any polymer and, as such, most propitious for study of régime III crystallization. For a medium M.wt. polymer, a régime II → III transition was obtained at 208°C using values of transport parameters common to many polymers ( U∗ = 1400 cal mol −1 , T ∞ − T g = 30°C) together with experimentally determined values of T 0 m(315°C) and T g(92°C). Under these conditions, the régime III/II slope ratio was found to be 2.07 (i.e. only 3.5% higher than predicted by régime theory), and reasonable estimates of surface free energies and of the work of chain folding were obtained. Other choices of the transport terms, including WLF and zero values, did not allow successful kinetic analyses. Although a régime I → II transition is predicted to occur at the high-temperature end of our growth-rate data, we found no experimental evidence for it. For a low M.wt. polymer, our analysis showed that régime III kinetics is obeyed at low temperatures, while at higher ones there is a continuous departure from that behaviour without, however, full attainment of régime II kinetics.