Key functions analysis of a novel nonlinear optical D-π-A bridge type (2E)-3-(4-Methylphenyl)-1-(3-nitrophenyl) prop-2-en-1-one chalcone: An experimental and theoretical approach

Abstract

In the current work a new third-order nonlinear optical organic single crystal of (2E)-3-(4-Methylphenyl)-1-(3-nitrophenyl) prop-2-en-1-one (ML3NC) has been grown with well-defined morphology using the slow evaporation solution growth technique. X-ray diffraction technique was used to confirm the crystal system. The presence of functional groups in the molecular structure was identified by robust FT-IR and FT-Raman spectra by experimental and theoretical analysis. The ultraviolet-visible-near infrared and photoluminescence studies shows that the grown crystals possess excellent transparency window and green emission band (∼560 nm) confirms their use in green OLEDs. The third-order nonlinear and optical limiting studies have been performed using femtosecond (fs) Z-scan technique. The third-order nonlinear optical susceptibility (χ(3)), second-order hyperpolarizability (γ), nonlinear refractive index (n2) and limiting threshold values are found to be 4.03 × 10−12 esu, 14.2 × 10−32 esu, −4.33 × 10−14 cm2/W and 2.41 mJ/cm2, respectively. Furthermore, the quantum chemical studies were carried out to achieve the ground state molecular geometry and correlate with experimental results. The experimental value of absorption wavelength (λabs = 328 nm) is found to be in excellent accord with the theoretical value (λabs = 328 nm) at TD-DFT/B3LYP/6-31G* level of theory. To understand the static and dynamic NLO behavior, the polarizability (α) and second hyperpolarizability (γ) values were determined using TD-HF method. The computed second hyperpolarizability γ(-3ω; ω,ω,ω) at 800 nm wavelength was found to be 0.499 × 10−32 esu which is in good agreement with experimental value at the same wavelength. These results confirms the applied nature of title molecule in optoelectronic and nonlinear optical devices.