Abstract
Inkjet printing of kesterite Cu2ZnSnS4 (CZTS) thin films on glass from molecular ink is described. CZTS ink consists of copper acetate, zinc acetate, tin chloride and thiourea dissolved in a mixture of ethylene glycol and isopropyl alcohol. The printed precursor films are vacuum dried and thermolysed at 200 °C in air to obtain CZTS films. X-ray diffraction and Raman spectroscopy of films confirm the formation of kesterite CZTS without any secondary phases. The band gap of the films is 1.48 eV as deduced from transmission spectrum using Tauc plot. The films are p-type with hole density and mobility of 2.65 × 1019 cm−3 and 0.3 cm2V−1s−1, respectively. Measurement of electrical conductivity of films in the temperature range from 77 to 300 K show that dominant mechanisms of conduction are Mott-Variable Range Hopping, Nearest Neighbour Hopping and Thermally Activated Band Conduction in the temperature ranges of 77–155 K, 180–240 K and 250–300 K, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.