Abstract
Material ductile fracture toughness can be described by J-integral versus crack extension relationship (J-R curve). As a conventional J-R curve measurement method, unloading compliance (UC) becomes impractical in elevated temperature testing due to relaxation of the material and a friction induced back-up shape of the J-R curve. In addition, the UC method may underpredict the crack extension for standard disk-shaped compact (DC(T)) specimens. In order to address these issues, the normalization method and direct current potential drop (DCPD) technique were applied for determining J-R curves at 24 C and 500 C for 0.18T DC(T) specimens made from type 316L stainless steel. For comparison purchase, the UC method was also applied in 24 C tests. The normalization method was able to yield valid J-R curves in all tests. The J-R curves from the DCPD technique need adjustment to account for the potential drop induced by plastic deformation, crack blunting, etc. and after applying a newly-developed DCPD adjustment procedure, the post-adjusted DCPD J-R curves essentially matched J-R curves from the normalization method. In contrast, the UC method underpredicted the crack extension in all tests resulting in substantial deviation in the derived J-R curves manifested by high Jq values than the normalization ormore » DCPD method. Only for tests where the UC method underpredicted the crack extension by a very small value, J-R curves determined by the UC method were similar to those determined by the normalization or DCPD method.« less
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.