Abstract
Superconductor-insulator-ferromagnet-superconductor (SIFS) Josephson tunnel junctions based on Nb/Al <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> /NiCu/Nb stacks with a thickness step in the metallic NiCu interlayer were fabricated. The step height of a few 0.1 nm was defined by optical lithography and controlled etching of both Nb and NiCu layers. Experimentally determined junction parameters by current-voltage characteristics and Fraunhofer pattern indicate a uniform NiCu thickness and similar interface transparencies for etched and non-etched parts. The critical current diffraction pattern was calculated and measured for stepped junctions having the same ground phase difference but different critical current densities in both halves. The measured data show a good agreement with simulations.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.