Abstract
C/SiC composite and TC4 alloy were successfully brazed using 70Ag28Cu2Ti (wt. %) as filler metal at 820 °C~920 °C for 5 min ~30 min. The effects of brazing parameters on the microstructures, phase composition, shear strength of the brazed joints were investigated by SEM, XRD. The mechanical performances of the brazed joints were measured by a universal mechanical testing machine. The results show that successful joining of C/SiC composite and TC4 alloy owes to interfacial reactions between the brazing alloy and the parent materials, and resultantly produce TiC, Ti5Si3 and Ti-Cu serial compounds at the interfaces; the interfacial structure of the brazed joint is C/SiC composite / TiC / Ti5Si3 /Ag (s.s) +Cu (s.s) / TiCu2 / Ti3Cu4 / TiCu / Ti2Cu / TC4 from C/SiC composite side to TC4 alloy side; the maximum shear strength of the brazed joint is 53.3 MPa at 860°C for 10min.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.