Joining and characterization of SS-430 using microwave hybrid heating technique

Abstract

Purpose The purpose of this paper is to based upon the joining and characterization (mechanical and metallurgical) of ferritic stainless steel (SS)-430 using a microwave hybrid heating (MHH) phenomenon. Design/methodology/approach The preliminary experiments were conducted using nickel-based powder as interface material using a domestic microwave oven at a frequency of 2.45 GHz and 900 W power for 720 s. The processed joint was metallurgically characterized by means of X-ray diffraction, Energy-dispersive X-ray spectroscopy and Field emission scanning electron microscopy. Mechanical characterization was done by means of tensile and Vickers’ microhardness testing to check the hardness and strength of the joint. Findings The metallurgical study revealed that the microstructure and formation of numerous phases of Fe2Si3 accompanied by chromium and nickel carbides. The average hardness of 359 Hv at the center of the joint and 637 Hv around the boundaries of the joint was observed. The tensile strength of the joint was observed to 471 MPa with an elongation of 9.02%. The worn surface of the joint signifies the presence of plastic deformation and it was limited due to the presence of harder phases such as Ni3Si and Ni3C. Research limitations/implications The concept of microwave joining of metals is a very challenging task as the temperature can not be controlled in the inert atmosphere of the microwave. It has been also observed that at certain elevated temperatures, the material starts absorbing the microwaves; which is unknown. So, a more intensive study is required to overcome these kinds of limitations. Practical implications MHH technique can be used to process different materials such as ceramics, composites and polymers. SS-430 joined by microwave heating is highly corrosion resistive and has wide applications in refrigerators cabinet panels, dishwasher linings, chimney liners, lashing wires, etc. Originality/value As of the author’s best knowledge, no work has been reported on the joining of SS-430 which has huge potential in the industries. Also, no work has been reported on the characterization of microwave joined SS-430.