Isothermal oxidation and TGO growth behaviors of YAG/YSZ double-ceramic-layer thermal barrier coatings

Abstract

In this study, yttrium aluminum garnet/yttria-stabilized zirconia (YAG/YSZ) double-ceramic-layer thermal barrier coatings (DCL TBC) and yttria-stabilized zirconia (YSZ) single-ceramic-layer thermal barrier coatings (SCL TBC) were deposited by atmosphere plasma spray (APS) on the Inconel 738 alloy substrate, and isothermal oxidation tests were performed to investigate the formation and growth behavior of thermally grown oxide (TGO). Results showed that the Al2O3 TGO thickness of both TBC groups increased by increasing the isothermal oxidation time，and then slowly decreased with the appearance and growth of the adverse multilayer structure comprising CoCr2O4, (Ni,Co)Al2O4, NiCr2O4, and NiO mixed oxides. However, since the significant inhibition effect of the YAG coating to oxygen ionic diffusion, the mixed oxides appearance time and TGO growth behaviors were delayed in the DCL TBC. As a result, the TGO thickness of the DCL TBC was always smaller than that of the SCL TBC in the entire oxidation process. And the Al2O3 layer thickness proportion in the total TGO of the DCL TBC was greater than or equal to that of the SCL TBC after oxidation for the same period. The results of weight gain showed that compared with the SCL TBC, the parabolic oxidation rate of the DCL TBC was decreased approximately 35%. Consequently, the DCL TBC has better high-temperature oxidation resistance than the SCL TBC.