Abstract
A study of the low-carbon steel with high hardenability was carried out. The steel contained the following alloying elements, wt. %: C – 0.20; Cr – 2.0; Mn – 2.0; Si – 1.04 Ni – 1.0; Mo – 0.3. The quenching – partitioning treatment of the studied steel was implemented. The microstructure of the steel consisted of the tempered martensite laths, bainite and martensite-austenite regions. The amount of the residual austenite and the carbon concentration in the residual austenite were estimated. The possibility of the quenching – partitioning treatment of the carburized steel was shown.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.