The high-temperature solution nitriding process is a suitable treatment for producing high-nitrogen steels by the diffusion of nitrogen from the surface to the center of steels under high nitrogen pressure at high temperatures. On the other hand, long-term solution nitriding at high temperatures can cause the formation of coarse-grained austenite. This study focused on the grain size, strength, and elongation properties of Fe-Cr-Mn high-nitrogen austenitic steels by isothermal aging. For this purpose, we produced high-nitrogen steels by three-step phase transformations: (i) high-temperature solution nitriding, (ii) isothermal aging, and (iii) reaustenitization. After solution nitriding, high-nitrogen austenitic steel was treated with isothermal aging to induce austenite decomposition. Supersaturated austenite (ϒ) transformed to less nitrogen-saturated austenite (ϒ′) and discontinuous cellular precipitation (DCP) during the isothermal aging treatment. Subsequently, the decomposed structure was reversed into austenite through reaustenitization. The results suggested that austenite grain refinement and increasing hardness were achieved by nucleating reversed austenite grains after reaustenitization treatment. On the other hand, a noticeable increase in elongation appeared after reaustenitization treatment for 30 min.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.