Abstract
The aim of this work is to present correlations between Vickers indentation cracks and fracture toughness of an Al 3Nb + Nb 2Al + AlNbNi in situ composite. Correlations between the resulting crack parameters and indentation load suggested that the radial-median model resulted in a better fit to the experimental data. The hardness value was found to change according to the indentation load applied. Low indentation loads resulted in high hardness values, while the application of higher loads decreased the hardness. Experimental results indicate that Vickers hardness varied from 8.6 to 9.5 GPa, which is due to the indentation size effect (ISE). Fracture toughness was calculated based on several models and the results were found to vary in a broad range of values. The fracture toughness obtained from Vickers indentation was in the order of 1.65–2.26 MPa m 1/2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.