Abstract
In order to reveal the effect of irradiation damage caused by high-level liquid radioactive wastes on the welded joint of the container, the irradiation-induced microstructure evolution and mechanical properties degradation of the 310S stainless steel welded joints were investigated in this study. For this purpose, the 1.3 MeV 60Co and 2 MeV accelerators were used to simulate irradiation experiments on 310S welded joints. The uniaxial tensile tests characterized the specimens' mechanical properties and fracture morphology. The results revealed that elongation was reduced by about 5% of irradiation damage by 60Co, and the fracture morphology shows a large number of secondary cracks. In contrast, the elongation was recovered irradiated by the accelerator, and the fracture morphology showed a large number of dimples. Following the interrupted creep deformation, creep fracture tests were conducted for irradiation specimens. The 60Co irradiation damage significantly decreases the creep resistance, leading to deformation of creep, which is increased to 1.5 times that of those unirradiated specimens. At the same time, the ductility is seriously degraded for the irradiated creep fracture specimens. As a result, the creep fracture strain of 60Co specimens is reduced to 70% of that of unirradiated specimens. Further, ductility reduction was related to the irradiated hardening by 60Co, while Nano-indenter hardness was 5.9 GPa, higher by 44% than the unirradiated specimens. The results are shown in an enrichment of Cr, C and P elements at phase boundaries for 60Co irradiation specimens, while the magnitude of element segregation increased by the accelerator combination irradiation. Finally, the creep cracking analysis results show intergranular cracking was observed on the surfaces of the irradiated specimens, while the M23C6 has a primary relationship with the intergranular cracks. The synergic effect of irradiation promoted damage, and element segregation was the primary cause of the intergranular cracking of the 310S welded joints.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.