Abstract
Zirconium alloys used as cladding materials in nuclear reactors can exhibit accelerated irradiation induced growth, often termed linear growth, after sustained neutron irradiation. This phenomenon has been linked to the formation of <c>-component dislocation loops and to the concentration of interstitial solute atoms. It is well documented for the Zircaloys that Fe dissolves from second phase particles (SPPs) during irradiation thus increasing the interstitial solute concentration in the matrix. However, no progress has yet been made into understanding whether a similar process occurs for the newer ZIRLO™ alloys. We aim to overcome this shortcoming here by studying compositional changes in second phase particles in Low Tin ZIRLO™ after neutron and proton irradiation using energy dispersive X-ray (EDX) spectroscopy. Material irradiated to 18dpa (displacements per atom) using neutrons and to 2.3 and 7dpa by protons was investigated. The results show that Fe is lost from Zr–Nb–Fe-SPPs during both neutron and proton irradiation. Prior to irradiation, Fe was detected at the interface of β-Nb-SPPs. This Fe enrichment is also dispersed during irradiation. Qualitatively, excellent agreement was found regarding the elemental redistribution processes observed after proton and neutron irradiation.
Submitted Version (
Free)
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.