Abstract
Iron nanoparticles (FeNPs) have been successfully prepared by high-energy ball milling in air for various milling times from 1 h to 32 h. Their structure, particle size, elemental composition, magnetic, and inductive heating properties were investigated by means of x-ray diffraction (XRD) analysis, field-emission scanning electron microscopy, energy-dispersive x-ray (EDX) spectroscopy, vibrating-sample magnetometry, and magnetic induction heating, respectively. XRD analysis showed that the average crystallite size decreased to 11 nm after 10 h of milling, then remained almost unchanged for longer milling times. Coexistence of iron (Fe) and iron oxide (FeO) phases was detected after 12 h of milling. EDX analysis also confirmed the occurrence of oxidation, which can be reconciled with the corresponding decrease and increase in saturation magnetization (Ms) with milling time when exposed to oxygen and when annealed under H2 ambient due to oxygen reduction. The time-dependent magnetic and inductive heating responses of the FeNPs were investigated for prospective application in magnetic hyperthermia. The effect of varying the alternating-current (AC) magnetic field strength on the saturation heating temperature and specific loss power of FeNP-containing ferrofluid with concentration of 4 mg/mL was also studied and is discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.