Abstract
Electron-beam-induced effects in preamorphized Sr2Nd8(SiO4)6O2 were investigated in situ using transmission electron microscopy with 200-keV electrons at temperatures ranging from 380 to 780 K. Within the electron-irradiated area, epitaxial recrystallization was observed from the amorphous/crystalline interface toward the surface, with the rate of recrystallization increasing as temperature increased from 380 to 580 K. Structural contrast features (i.e., O deficient amorphous material), as well as recrystallization, were observed outside of the irradiation area at temperatures from 680 to 780 K. Ionization-induced processes and local nonstoichiometry induced by oxygen migration and desorption are possible mechanisms for the electron-beam- induced recrystallization and for the formation of the structural contrast features, respectively.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.