Abstract
A novel microporous polymer electrolyte (MPE) comprising blends of poly(vinylidene fluoride-cohexafluoropropylene) [P(VdF-HFP)] and polyethylene oxide (PEO) was prepared by phase inversion technique. It was observed that addition of PEO improved the pore configuration, such as pore size, pore connectivity and porosity of P(VdF-HFP) based membranes. The room temperature ionic conductivity was significantly enhanced. The highest porosity of about 65% and ionic conductivity of about 7 × 10−4 S cm−1 was obtained when the weight ratio of PEO was 40%. The liquid electrolyte uptake was found to increase with increase in porosity and pore size. However, at higher weight ratio of PEO (> 40%) porosity, pore size and ionic conductivity was decreased. This descending trend with further increase of PEO weight ratio was attributed to conglomeration effect of PEO at the pores.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.