Ionic Conductivity and Cycling Performance in PEO Polymer Electrolyte Enhanced by Non-Milled In Situ Nano-LLZO Powders.

Abstract

High Li+ conductivity, good interfacial compatibility, and nano-scale particle size have always been essential conditions for selecting inorganic fillers in high-performance composite solid electrolytes. In this study, non-milled in situ LLZO fillers with nanosize was synthesized via the sol-gel method by rapid heating sintering, which resulted in more surface defects and fewer impurities in LLZO. Compared with milled LLZO fillers, these non-milled LLZO fillers with more surface defects and fewer impurities can effectively reduce the crystallinity of PEO and agglomeration in PEO, which can form composite electrolytes with high Li+ conductivity. Most importantly, the discharge capacity of the 7.5% non-milled LLZO-PEO-based LiFePO4/Li battery is about 135.5 mA h g-1 at 1C and 60 °C. After 100 cycles, the discharge specific capacity remains at 99%. It is worth noting that nano-sized non-milled LLZO will improve the discharge capacity of LiFePO4/Li batteries to 122.1 mA h g-1 at 0.2C and 30 °C.