Abstract

Electrolytes comprising poly(ethylene carbonate) (PEC)/poly(trimethylene carbonate) (PTM C) with lithium bis(trifluoromethane sulfonyl)imide (LiTFSI) are prepared by a simple solvent casting method. Although PEC and PTMC have similar chemical structures, they are immiscible and two glass transitions are present in the differential scanning calorimetry (DSC) measurements. Interestingly, these two polymers change to miscible blends with the addition of LiTFSI, and the ionic conductivity increases with increasing lithium salt concentration. The optimum composition of the blend electrolyte is achieved at PEC6 PTMC4 , with a conductivity as high as 10-6 S cm-1 at 50 °C. This value is greater than that for single PEC- and PTMC-based electrolytes. Moreover, the thermal stability of the blend-based electrolytes is improved as compared to PEC-based electrolytes. It is clear that the interaction between CO groups and Li+ gives rise to a compatible amorphous phase of PEC and PTMC.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.