Abstract
CsPbBr3:Mn NCs were synthesized via a hot injection method to test the anion exchange reaction using ZnCl2 and benzoyl chloride. In the case of no ion exchange reaction, Mn-doping resulted in the photoluminescence (PL) efficiency of the NCs increased from 62.4 to 82.9% and the stability greatly improved even though no Mn emission was observed. The NCs maintained the initial cubic phase structure. Interestingly, the ion exchange reaction using benzoyl chloride resulted in the host excitation to Mn2+ d-d transition. Bright Mn ion orange-emission was observed. The mild ion exchange reaction of benzoyl chloride greatly improved the stability of the NCs compared with ZnCl2. To use the bright Mn ion emission, a white light-emitting diodes (LED) with a color coordinates of (0.320, 0.319) and color temperature of 5706 K was created using CsPbBr3:Mn NCs. The result provides an effective route to obtain high-performance white LED materials.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.