Abstract
The formation of Au nanoclusters in MgO using ion implantation and subsequent annealing was investigated. Approximately 1200 and 1400 Au2+ ions/nm2 were implanted in MgO(100) substrates at 300 and 975 K, respectively. Subsequent annealing in air for 10 h at 1275 K promoted the formation of Au nanostructures in MgO. The sample implanted at 300 K showed severe radiation damage. In addition, two-dimensional plateletlike structures with possible composition of Au and MgO were formed during implantation in the sample that was implanted at 300 K. In contrast, Au implantation at 975 K promoted the nucleation of Au nanostructures during implantation. Subsequent annealing of both samples show three-dimensional clusters in MgO. However, the 975 K implanted sample shows clean, high-quality, single-crystal Au clusters that have an epitaxial relationship to MgO(100).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.