Abstract
During the last decade, research on metal oxide nanostructures has led to the emergence of new materials with unique physical and chemical properties. In this work, we report on a process based on an atmospheric pressure micro-afterglow to synthesize oxide nanostructures of copper-iron alloy thin films deposited by magnetron sputtering. In plasma afterglow processes, active species like oxygen atoms or metastable states of oxygen are available. They are more active than ground state oxygen at low temperature because of the extra amount of energy coming from dissociation or excitation. Oxidation of metals in these conditions promotes the growth of oxide nanostructures.The effect of the addition of copper to iron (and vice versa) is investigated by creating either alloys single layers or stacks of copper and zinc layers with different thicknesses on a glass substrate. The experimental device consists in using an Ar-O2 microwave plasma. Active species exit the reactor through a tiny hole (500 µm in diameter) and react with the copper-iron film to perform the direct synthesis of oxide nanostructures in a single step without any template or surfactant. The morphology, shape and size distribution can be controlled by varying the experimental parameters such as the amount of oxygen injected in the plasma, the microwave power, the treatment time or the alloy composition. It appears possible to synthesize different kinds of nanostructures with good reproducibility in a single-step process: nanowires, nanowalls or nanoblades. Various characterization means, including SEM, SIMS, TEM and XRD were used to determine the composition of the nanostructures. Besides, XPS microscopy experiments were carried out with the SPEM at the spectroscopy for chemical analysis (ESCA) microscopy beamline at the Elettra synchrotron facility in Trieste. We show that both oxides, CuO and Fe2O3, can be formed on the same spot (see figure). Furthermore, by controlling the composition of the alloy, we show that very thin CuO nanowires (with diameters as small as 5 nm) can be grown. Ultra-thin nanoblades of Fe2O3 can be formed. They are so thin than their edge is submitted to grow instabilities and become serrated.The formation mechanism of these structures was investigated. The role of the addition of a new element on the growth mechanism, together with the way it is distributed within the stack, will be discussed. The role of stress on grain size, grain boundaries and outward diffusion of metallic ions will be discussed. Results will be compared to those obtained by different groups via thermal oxidation. Finally, a growth model will be proposed to explain the synthesis of the as-grown nanostructures. Figure 1
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have