Investigations on the effect of 100 MeV Ni ions irradiated chloride vapour phase epitaxy (Cl-VPE) grown GaN epilayers

Abstract

Gallium nitride (GaN) epilayers have been grown by chloride vapour phase epitaxy (Cl-VPE) technique and the grown GaN layers were irradiated with 100 MeV Ni ions at the fluences of 5 × 10 12 and 2 × 10 13 ions/cm 2. The pristine and 100 MeV Ni ions irradiated GaN samples were characterized using X-ray diffraction (XRD), UV-visible transmittance spectrum, photoluminescence (PL) and atomic force microscopy (AFM) analysis. XRD results indicate the presence of gallium oxide phases after Ni ion irradiation, increase in the FWHM and decrease in the intensity of the GaN (0 0 0 2) peak with increasing ion fluences. The UV-visible transmittance spectrum and PL measurements show decrease in the band gap value after irradiation. AFM images show the nanocluster formation upon irradiation and the roughness value of GaN increases with increasing ion fluences.