Abstract
Accelerated thermal aging experiments were conducted on butyl rubber materials in order to investigate aging behavior using X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), positron annihilation lifetime spectroscopy (PALS), and differential scanning calometry (DSC). The XPS results suggested that the thermal oxidation process took place heterogeneously along the samples thicknesses. The aging mechanism was identified to be crosslinking by means of the combined use of PALS and DSC results. Lifetime and intensity of ortho-positronium (o-ps) diminished, and the glass transition temperature (T g ) increased during aging. The dispersion condition of silica particles, observed by SEM images, showed that the filler agglomerated after aging. Time temperature superposition was carried out using compression set measurements in the temperature range of 100 to 60 °C. The Arrhenius plot clearly exhibited a curvature around 75 °C, and the activation energy dropped from 126.7 to 58.8 kJ/mol across this region. Relative importance of different processes, over the entire temperature range, was discussed; lifetime at room temperature was predicted. Open image in new window
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.