Abstract
Large NdP 5 O 14 crystal with dimension of 15 2 25 2 60 mm 3 has been grown by flux method. The spontaneous strains and ferroelastic domain structures have been investigated by high resolution X-ray diffractometry for the first time. The reflection peak separations resulting from the misorientation between matrix domain and ferroelastic domain were observed in the rocking curves for several different reflections. Based on the features of the reflection peak separations, the ferroelastic domain structures were determined. It is found that most of the ferroelastic domains in NdP 5 O 14 are of type-a, while type-b ferroelastic domains only appear in the serious strain regions. Based on the domain structures of NdP 5 O 14 , the reflection peak separations for 802, 402 and 204 reflections were calculated respectively. And the experimental observations are in agreement with the calculations very well. In addition, the spontaneous strain in NdP 5 O 14 was determined to be 0.0082 by measuring the peak separation between two 800 diffraction from the matrix domain and the ferroelastic domain respectively. A detailed discussion on domain structures in the crystal is given in terms of structural and symmetric analyses.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.