Abstract
We report on morphological, optical, and lasing characteristics of InAs quantum dots (QDs) embedded in an In0.69Ga0.31As0.67P0.33 quantum well (having a bandgap energy corresponding to a wavelength of 1.35μm (1.35Q-InGaAsP)), which formed a dot-in-a-well (DWELL) structure. This DWELL was further sandwiched in In0.85Ga0.15As0.32P0.68 layers (1.15μm, 1.15Q-InGaAsP). A 2 monolayer-thick GaAs layer was simultaneously introduced right below the InAs QD layer in the DWELL structure (GDWELL). The emission wavelength of the InAs GDWELL was 1490nm, which was slightly shorter than that of the InAs QDs embedded only in 1.15Q-InGaAsP layers. To evaluate the effects of the GDWELL structure on lasing characteristics, gain-guided broad-area (BA) and index-guided ridge-waveguide (RW) laser diodes (LDs) were fabricated. The BA-LDs with the InAs QDs embedded only in 1.15Q-InGaAsP layers did not show the lasing at room temperature (RT) even in pulsed mode. For the GDWELL structure, however, the lasing emissions from both the BA-LDs and RW-LDs were successfully achieved at RT in continuous-wave mode.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.