Investigation on the Effects of Acetone Vapor-Polishing to Fracture Behavior of ABS Printed Materials at Different Operating Temperature

Abstract

Fused Deposition Modelling (FDM) technology is one of most common technique used in 3D printing as of today for several reasons such as it is low cost and high speed printing capacity. However, common characteristic of FDM 3D printed materials are poor layer adhesion strength and rough surface finish which requires post-processing to improve it. Heat treatment and vapor-polishing are post-processing techniques used to address the poor layer adhesion and rough surface finish of 3D printed materials, respectively. This study will combine these two post-processing techniques and investigate its effect on the mechanical properties of 3D printed materials. The present study describes the effect of acetone vapor-polishing to facture behavior of ABS 3D printed material at higher operating temperatures. The study will compare the fracture behavior of ABS 3D-printed material when polished using acetone vapor bath and tested at high operating temperature to unpolished material. Five replications for each test condition were conducted. All experiment was carried out using ASTM Izod Type E tests with a 2.75J pendulum. The results showed that acetone vapor polishing strongly affects the fracture behavior of ABS 3D printed materials when operating at high temperature.