Abstract
This study is focused on 3D printing of polyamide 6 (PA6), PA6/graphene oxide (PA6/GO) and PA6/glass-fibre-reinforced (PA6/GF) composites. The effect of graphene oxide and glass-fibre reinforcement on 3D-printed PA6 is explored for improvement of the interfacial bond and interlaminar strength in ambient, wet and high temperature conditions relating to electric car battery box requirements. The influence of environmental conditions and process parameters on the 3D-printed polymer composites quality is also examined. Commercial PA6 filament was modified with GO to investigate the thermal and mechanical properties. The modified composites were melt-compounded using a twin-feed extruder to produce an improved 3D-printing filament. The improved filaments were then used to 3D-print test samples for tensile and compression mechanical testing using universal testing machines and thermal characterisation was performed following condition treatment in high temperature and water for correlation to dry/ambient samples. The study results show the studied materials were mostly suitable in dry/ambient conditions. PA6/GF samples demonstrated the highest strength of all three samples in ambient and high-temperature conditions, but the least strength in wet conditions due to osmotic pressure at the fibre/matrix interface that led to fibre breakage. The introduction of 0.1% GO improved the tensile strength by 33%, 11% and 23% in dry/ambient, dry/high temperature and wet/ambient conditions, respectively. The wet PA6/GO samples demonstrated the least strength in comparison to the ambient and high-temperature conditions. Notwithstanding this, PA6/GO exhibited the highest tensile strength in the wet condition, making it the most suitable for a high-strength, water-exposed engineering application.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.