Abstract
Cr4Mo4Ni4V steel has excellent fracture toughness and fatigue life, which is one of the main materials for the new generation of aeroengine bearing rings. However, there is still lack of investigation on hot processing of Cr4Mo4Ni4V steel up to now. Herein, the hot processing map is established based on systemic compression tests; then, according to the requirements of Cr4Mo4Ni4V steel for carbide content, improved hot processing map is established based on the carbide content by superimposing the carbide content zoning map. Results reveal that the activation energy is 304.9 kJ mol−1, and power dissipation value increases only within the strain range of 0.2–0.4, while the instability zone always moves toward the direction of high strain rate with the increase of strain. In 900–1150 °C, 0.01–5 s−1, the content of carbide could be divided into three zones: little dissolved zone, mostly dissolved zone, and completely dissolved zone. Improved hot processing map indicates that the ideal processing domain is 950–1050 °C, 0.01–0.3 s−1 etc.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.