Abstract
An attempt has been made to assess the grinding wear behaviour of austempered ductile iron (ADI) as media material in comminution of Kudremukh haematite iron ore in a ball mill. Spheroidal graphite (S.G) iron balls were austenitised at 900°C for one hour and austempered at 280°C and 380°C for different time durations. These materials were characterized by measuring hardness, carrying out X-ray diffraction analysis, studying microstructures using scanning electron microscope (SEM). Grinding wear behaviour of ADI was assessed during wet grinding at different pH of the mineral slurry. The wear resistance of ADI was compared with that of forged En 31 steel balls under similar grinding conditions. It was found that ADI balls austempered at 280°C for 30 minutes which contains lower bainite registered superior wear resistance. It was also noted that the wear resistance of ADI was more at higher pH range of the slurry.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.