Abstract

PurposeThe foundry industry incurs additional costs as a result of defective castings. Shrinkage defects are a frequent problem in ductile iron castings. It is still essential to understand how shrinkage porosity varies in size when the ductile iron composition changes. This information can be used to produce high-quality cast parts and determine the best processing conditions. The objective of this research paper is to examine the effect of carbon equivalent and inoculation on the morphology of the shrinkage defect using thermal analysis.Design/methodology/approachThis study focuses on certain thermal analysis parameters, such as the angle of the first derivative curve at the solidus temperature, recalescence and its relationships to graphite nucleation and shrinkage tendency. The results of thermal analysis in terms of the cooling curve and its derivative parameters, and thorough characterizations of the shrinkage observed in cup castings produced with various melt compositions and inoculation are presented in the current study.FindingsThe proportion of caved surfaces and macro shrinkage porosity defects has been reduced as the carbon equivalent of melt increases from hypoeutectic to a hypereutectic composition. The composition that is slightly hypereutectic has the lowest shrinkage propensity. Although inoculation reduces shrinkage, the importance of this parameter differs depending on the carbon equivalent.Originality/valueThe percentage of macro shrinkage porosity and the angle that the cooling rate curve forms are strongly correlated. It is found that the macro shrinkage size decreases as the angle of the first derivative curve at the solidus temperature is reduced. Further, lower macroporosity is produced by a metal that has a higher nodule count in association with a greater cooling rate toward the end of the solidification process.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call