Abstract
High quality Nb doped SrTi1−xNbxO3 polycrystalline ceramics were fabricated using a conventional solid state reaction method. By annealing in a reducing atmosphere at an elevated temperature, a series of Nb and oxygen vacancy co-doped SrTi1−xNbxO3−δ (0 ⩽ x ⩽ 0.2) samples was obtained. The thermoelectric properties of the samples were measured in the temperature range from 15 K to 380 K. These measurements showed that the transport behavior of these samples is consistent with the small polaron conduction mechanism for the temperature range from room temperature to 380 K. Furthermore, after annealing, samples with a lower Nb doping were found to give a relative higher ZT value, while excess Nb led to a reduced ZT value. The x = 0.02 sample gave the optimal thermoelectric properties, with a ZT value of 0.023 at 300 K, and 0.028 at 380 K.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.