Abstract
ABSTRACTStructure and mechanical properties of binary Ti-TM (TM-other transition metals) and ternary Ti-Fe-(TM, B or Si) alloys produced in the shape of the arc-melted ingots of about 25 mm diameter and 10 mm height are studied. The formation of high-strength and ductile hypereutectic alloys was achieved in the Ti-Fe, Ti-Fe-Cu and Ti-Fe-B systems. The structures of the high-strength and ductile hypereutectic alloys studied by X-ray diffractometry and scanning electron microscopy were found to consist of the primary cubic Pm3 m intermetallic compound (TiFe-phase or a solid solution on its base) and a dispersed eutectic consisting of this Pm3m intermetallic compound + BCC Im 3 m β-Ti supersaturated solid solution phase. The hypereutectic Ti-Fe alloy showed excellent compressive mechanical properties. The addition of Cu improves its ductility. B addition increased mechanical strength. Ni, Cr and Mn additions caused embrittlement owing to the formation of alternative intermetallic compounds. The deformation behaviour and the fractography of the Ti-based alloys were studied in details. The reasons for the high strength and good ductility of the hypereutectic alloys are discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.