Abstract
In this study, we demonstrate the optimization of the annealing temperature for enhanced thermoelectric properties of ZnO. Thin films of ZnO are grown on a sapphire substrate using the metal organic chemical Vapor Deposition (MOCVD) technique. The grown films are annealed in an oxygen environment at 600–1000°C, with a step of 100°C for one hour. Seebeck measurements at room temperature revealed that the Seebeck coefficient of the sample that was not annealed was 152 μV/K, having a carrier concentration of N D ~ 1.46 × 1018 cm–3. The Seebeck coefficient of the annealed films increased from 212 to 415 μV/K up to 900°C and then decreased at 1000°C. The power factor is calculated and found to have an increasing trend with the annealing temperature. This observation is explained by the theory of Johnson and Lark–Horovitz that thermoelectric properties are enhanced by improving the structure of ZnO thin films. The Hall measurements and PL data strongly justify the proposed argument.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.