Abstract
Laser powder bed fusion (LPBF) is an advanced manufacturing technology; however, inappropriate LPBF process parameters may cause printing defects in materials. In the present work, the LPBF process of Ti-6.5Al-3.5Mo-1.5Zr-0.3Si alloy was investigated by a two-step optimization approach. Subsequently, heat transfer and liquid flow behaviors during LPBF were simulated by a well-tested phenomenological model, and the defect formation mechanisms in the as-fabricated alloy were discussed. The optimized process parameters for LPBF were detected as laser power changed from 195 W to 210 W, with scanning speed of 1250 mm/s. The LPBF process was divided into a laser irradiation stage, a spreading flow stage, and a solidification stage. The morphologies and defects of deposited tracks were affected by liquid flow behavior caused by rapid cooling rates. The findings of this research can provide valuable support for printing defect-free metal components.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.