The closed porous structure in ceramic materials is investigated by spin-echo small-angle neutron scattering. A series of ceramic samples of oxygen–ion conductors based on bismuth molybdate with the general formula Bi12.8X0.2Mo5O34 ± δ (X = Mg, Ba, Ca, Sr) is obtained by powder sintering for 6−45 h at a temperature close to the melting point. The samples are characterized by scanning electron microscopy and X-ray fluorescence analysis. It is found that they had a stoichiometric chemical composition, are singlephase, and contain clean pores between crystal grains. The pore size is determined by spin-echo small-angle neutron scattering and ranges from 2.2 to 3.5 μm. It is demonstrated that longer sintering times correspond to larger pores (the increase in their average diameter is as large as 30%). It is found that the studied materials lack a fractal pore structure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Surface Investigation: X-ray, Synchrotron and Neutron Techniques
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.