Abstract
A dynamic loop test method for measuring strain rate-dependent fiber properties was developed. During dynamic loop testing, the fiber ends are accelerated at constant levels of 20.8, 50 and 343 m/s2. The test method is used to study Kevlar® KM2-600, which fails in axial compression due to kink band formation. The compressive failure strain and strain rate at the onset of kink band formation is calculated from the critical loop diameter ( D C), which is monitored throughout the test using a high-speed camera. The results showed that compressive failure strain increases with strain rates from quasi-static to a maximum strain rate of 116 s−1 by a factor of ∼3. Kink angles (φ) and kink band spacing ( D S) were 60 ° ± 2 ° and 16 ± 3 μm, respectively, over the strain rates tested. Rate-dependent mechanisms of compressive failure by kink band formation were discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.