Investigation of Surfactant Type, Dosage and Ultrasonication Temperature Control on Dispersity of Metal-Coated Multi-Walled Carbon Nanotubes

Abstract

We studied the dispersity of multi-walled carbon nanotubes (MWNTs) combined with different metal- lic particles (Ni and Fe). An ultrasonic-assisted water-bath dispersion process was used to dis- perse the metal-coated MWNTs in different solutions and the dispersity was measured using an ultraviolet-visible spectrophotometer. The dispersity and morphology of the MWNTs were characterized using field-emission scanning electron microscopy (FE-SEM) together with digital image processing technology. Effects of dispersant type (sodium dodecyl benzene sulfonate (SDBS), oleic acid, and polymer (TNEDIS)) and surfactant dosage on the dispersity of the metal-coated MWNTs were investigated under controlled and uncontrolled temperatures and results were compared with those from the untreated MWNTs. The results showed that the negative effects of temperature on the ultrasonic dispersion process could be eliminated through a temperature-controlled system. Moreover, the TNEDIS, SDBS, and oleic acid were arranged in the descending order of the dispersion effect degree. The untreated MWNTs, Ni-coated MWNTs, and Fe-coated MWNTs were arranged in the descending degree of dispersity order. Since the metal coating makes the MWNTs harder and more fragile, the metal-coated MWNTs are more likely to fracture during the ultrasonic dispersion process.