Abstract
Undoped ZnO film and ZnO films, which are co-doped with F and In (FIZO) at different concentrations, were synthesized by sol–gel technique and the effects of co-doping of F and In on structural and optical properties of ZnO thin films were investigated. The concentration ratio of [F]/[Zn] was altered from 0.25 to 1.75 with 0.50 step at.% mole and [In]/[Zn] was altered from 0.25 to 1.00 with 0.25 step at.% mole. X-ray diffraction analysis indicates that the films have polycrystalline nature and the (002) preferred orientation is the stronger peak. No extra phases involving zinc, fluorine and indium compounds were observed even at high F and In content. The grain size of undoped ZnO and FIZO thin films varied between 15 and 20nm with a small fluctuation. From the SEM images, although the undoped ZnO had a smooth and particle-shaped surface, FIZO films had nanofiber-networks shapes over the surface with average size of 500nm. The surface morphologies and crystallite sizes for the F and In doped films were slightly different from than those of undoped film. From the optical study, a slight shrinkage of band gap was backwardly observed from 3.36 to 3.25eV with the increasing of F and In content.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.