Abstract
In recent years, with the growing demand for non-contact and real-time optical temperature measurements, it has become imperative to develop new luminescent thermometry materials as well as novel temperature detection schemes with higher sensitivity. In this work, a series of Sr1-xB4O7:xTm2+ (x = 0.001-0.01) polycrystalline powder samples were prepared using a high temperature solid state reaction under ambient atmospheric conditions. The emission spectra and the luminescence decay curves of the red emission corresponding to the 4f125d → 4f13(2F7/2) transition of Tm2+ were recorded at intervals of 10 K from 280 K to 380 K. Both the emission intensity and the fluorescence lifetime exhibited remarkable temperature correlation in the studied temperature range, which reached the best relative temperature sensitivities of 3.55% K-1 and 3.86% K-1 at 363 K and 346 K, respectively. Furthermore, taking into account the highly sensitive variation of the fluorescence lifetime of Tm2+ in the SrB4O7 matrix as the temperature increased near room temperature, a time-resolved temperature measurement scheme was performed to realize real-time temperature field imaging. By utilizing the intensified charge coupled device (ICCD) camera with a time gate to acquire the integral intensity of distinct time intervals and calibrate the relationship between the ratio and the temperature, the experimental results demonstrated that this temperature measurement scheme can achieve a maximum relative sensitivity of 9.39% K-1 at 313 K, which significantly surpasses the relative sensitivity of the other two conventional temperature measurement schemes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.