Abstract
Thermal spray coatings, especially WC-12Co, applied on galvanizing line hardware exhibit enhanced corrosion resistance in molten zinc environment. However, the service life of such coated components is usually reported up to 15 days. This work studies 30 days of prolonged performance for coatings like Cr3C2-NiCr, Al2O3, Al2O3-TiO2 and WC-12Co in molten zinc. Post-testing, stability of the coatings was assessed by corrosion products and phase analysis along with elemental mapping, surface morphology and porosity across top and cross sections and weight change data. Property evaluation of these coatings indicates better performance of oxide coatings, particularly Al2O3, as compared to carbide coatings.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.